| Customization: | Available |
|---|---|
| Ash Content: | Low Ash |
| Calorific Value: | High Calorific Value |
|
Still deciding? Get samples of US$ 1/kg
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Bulk density | ≥2.06/cm3 |
| Ash | ≤0.5% |
| V.M | ≤0.5% |
| S | ≤0.5% |
| Moisture | ≤0.5% |
| Fixed carbon | ≥98% |
CPC
CPC Calcined Petroleum Coke is mainly used in blast furnace iron smelting and blast furnace smelting of non-ferrous metals such as copper, lead, zinc, titanium, antimony.
Smelting industry, a small amount of calcium carbide, carbon disulfide, element phosphorus, etc. CPC Calcined Petroleum Coke powder is also used as a fuel for sintering in steel complexes.Coke is used as raw material for water gas synthesis.
High Fixed Carbon: 95% - 99%
Low Sulphur: 0.6% - 3%
Low Nitrogen
High Carbon Recovery: 90% - 97%
Low Ash: 0.5% - 5%
Low Volatile Matter: max. 1.5%
Specification:
(size: 0-1mm, 1-3mm, 3-5mm, 5-8mm, or at customer'demand)
| Models | F.C %(min) | Ash % (max) | V.M | S | Moisture |
| SID-95 | 95 | 4.5 | 1.0 | 0.25 | 0.3 |
| SID-94 | 94 | 5.0 | 1.0 | 0.25 | 0.3 |
| SID-93 | 93 | 6.5 | 1.2 | 0.3 | 0.5 |
| SID92 | 92 | 7.0 | 1.2 | 0.3 | 1.0 |
| SID-90 | 91 | 8.0 | 1.5 | 0.35 | 1.0 |
Calcined Petroleum Coke/Calcined Pitch Coke
Calcined Pitch coke is mainly used for metallurgy & foundry, it can improve the carbon content in steel-melting and casting, Also it can increase the quantity of scrap steel and reduce the quantity of pig iron, or use no scrap iron at all.
High carbon, low sulfur, low nitrogen,high graphitization degree,high carbon recovery (92% ~ 98%),with stable effect on improving the carbon content.
| Type | C | S | Moisture | Ash | Volatile | N PPM |
| Min/Max | Max | Max | Max | Max | Max | |
| FC-7 | 98.50% | 0.30% | 0.50% | 1% | 1% |
Application
Mainly used for manufacturing graphite electrode, carbon, silicon carbide, calcium carbide and other raw materials, can also be directly used for smelting, casting and forging process as fuel